Stress corrosion cracking probability of selective laser melted 316l austenitic stainless steel under the effect of grinding induced residual stresses

HIGHLIGHTS

• who: Arshad Yazdanpanah and collaborators from the Department of Industrial Engineering, University of Padova, Via Marzolo, Padova, Italy have published the research: Stress Corrosion Cracking Probability of Selective Laser Melted 316L Austenitic Stainless Steel under the Effect of Grinding Induced Residual Stresses, in the Journal: Metals 2021, 327 of /2021/
• what: In the current work, galvanostatic tests combined with SEM crosssectional analysis showed that SCC cracks initiation and propagation occurred within a short period along the melt pool boundaries.
• how: Surface roughness was measured on each condition and the results showed that with . . .
  

   

  